DESARROLLO DE MICROESTRUCTURA EN CEMENTOS MEZCLA ELABORADOS CON ARCILLAS CAOLINÍTICAS CALCINADAS DE MEDIANO GRADO: EFECTO EN INDICADORES DE DURABILIDAD
MICROSTRUCTURE DEVELOPMENT IN BLENDED CEMENTS MADE WITH MEDIUM-GRADE CALCINED KAOLINITIC CLAYS: EFFECT ON DURABILITY INDICATORS
Martín N. Humberto1, Alejandra Tironi1*, Alberto N. Scian2, Edgardo F. Irassar1 (1) Fac. de Ing., Centro de Investigaciones en Física e Ingeniería del Centro de la Prov. de Bs. As. (CONICET-CICPBA-UNCPBA), Av. Del Valle 5737, Olavarría – Argentina, (2) Centro de Tecnología de Recursos Minerales y Cerámica (CICPBA-CONICET La Plata-UNLP), Con. Centenario y 506 M.B. Gonnet (1897), Buenos Aires – Argentina
Resumen
El objetivo de este trabajo es evaluar la influencia del ordenamiento estructural de la caolinita presente en arcillas de mediano grado, calcinadas y molidas, en el desarrollo de la microestructura de pastas y su efecto en los indicadores de durabilidad. Para esto se utilizaron tres arcillas caoliníticas, luego se elaboraron cementos mezcla conteniendo 25% de arcillas calcinadas. Se estudió la evolución de la microestructura en pastas utilizando DRX, DTA/TG y MIP. Se determinaron dos indicadores de durabilidad en morteros a 28 días: velocidad de succión capilar y coeficiente de difusión de vapor de agua. Los resultados obtenidos muestran que, para arcillas con similar contenido de caolinita, la estructura desordenada de la caolinita favorecerá la resistencia al transporte de agua (menor volumen de poros con diámetro mayor a 60 nm), y no será favorable para el transporte de vapor de agua (mayor volumen de poros con diámetro menor a 30 nm).
Abstract
The objective of this work is to evaluate the influence of the structural arrangement of kaolinite present in medium grade clays, calcined and ground, on the development of the microstructure of pastes and its effect on durability indicators. For this purpose, three kaolinitic clays were used, then blended cements containing 25% of calcined clays were elaborated. The evolution of the microstructure in pastes was studied using XRD, DTA/TG and MIP. Two durability indicators were determined in mortars at 28 days: capillary suction velocity and water vapor diffusion coefficient. The results obtained show that, for clays with similar kaolinite content, the disordered structure of kaolinite will favor resistance to water transport (smaller pore volume with diameter greater than 60 nm) and will not be favorable for water vapor transport (larger pore volume with diameter less than 30 nm).
Palabras clave: arcillas caoliníticas calcinadas, microestructura, absorción de agua, difusión de vapor de agua Keywords: calcined kaolinitic clays, microstructure, water absorption, water vapor diffusion